SPECIFICATIONS
Flatness |
λ/8 @ 633 nm |
Parallelism |
< 20 arcsec |
Perpendicularity |
< 5 arcmin |
Angle tolerance |
< 30 arcmin |
Aperture tolerance |
± 0.1 mm |
Surface quality |
10-5 scratch & dig (MIL-PRF-13830B) |
Clear aperture |
>90% of full aperture |
Laser damage threshold |
>0.5 J/cm2, 133 fsec pulse, 800 nm typical, 50 Hz |
EKSMA OPTICS recommends BBO crystals of the following thickness depending on application and fundamental wavelength pulse duration, assuming it is spectrum limited Gausian pulse:
Application | Pulse duration, fs | Thickness, mm |
Type 1, THG@800 nm, θ=44.3°, φ=90° | 10 | 0.01 |
Type 1, THG@800 nm, θ=44.3°, φ=90° | 20 | 0.02 |
Type 1, THG@800 nm, θ=44.3°, φ=90° | 50 | 0.05 |
Type 1, THG@800 nm, θ=44.3°, φ=90° | 100 | 0.1 |
Type 1, THG@800 nm, θ=44.3°, φ=90° | 200 | 0.2 |
EKSMA Optics Femtoline BBO Crystals for Ti:Sapphire Frequency Conversion
121.54 kB |
Free Standing BBO Crystals
Crystals down to 100 µm thickness can be manufactured as free standing crystals (not attached to any kind of support). However, ring mounts are highly recommended for safe handling of these thin crystals. Minimum aperture of free standing BBO is 5x5 mm, maximum aperture is 22x22 mm. The tolerance is ±50 µm for crystals of thickness down to 300 µm and ±20 µm for crystals of thickness down to 100 µm.
Optically Contacted Crystals
BBO crystals less than 100 µm thickness can be supplied optically contacted on UV Fused Silica substrate sizes 10x10x1 mm or 12x12x2 mm. Other sizes of substrates are also available on request. Minimum aperture of optically contacted BBO is 5x5 mm, maximum aperture is 10x10 mm. The tolerance of crystal thickness is +10/-5 microns.
Protective Coatings for BBO Crystals
P-protective coating - is a single or two layer antireflection coating made at specified wavelength range. Typical reflection values are R<2% in the mid range, R<4% at the edges. P coating is highly recommended for ultrashort pulse applications and features low dispersion and very high laser damage threshold.