Dichroic Mirrors with High Transmission

Products

Specifications

Brochures

Description

Material

Diameter

Thickness

AOI

Reflected Wavelength

Transmitted Wavelength

Remove all filters

Code	Material	Diameter	Thickness	AOI	Reflected Wavelength	Transmitted Wavelength	LIDT @ 1064 nm	Price	Delivery	Add to cart
041-6215HT	UV FS	ø 12.7 mm	3 mm	45°	R>99.5%@976nm	T>98%@1030-1060nm	>3 J/cm²	303 $	Request
042-6215HT	UV FS	ø 25.4 mm	6 mm	45°	R>99.5%@976nm	T>98%@1030-1060nm	>3 J/cm²	351 $	4 - 5 days
041-6800HT	UV FS	ø 12.7 mm	3 mm	0°	R>99.5%@1064nm	T>98%@808nm	>10 J/cm²	212 $	Request
download PDF
i 042-6800HT	UV FS	ø 25.4 mm	6 mm	0°	R>99.5%@1064nm	T>98%@808nm	>10 J/cm²	266 $	4 - 5 days
download PDF
i 041-6805HT	UV FS	ø 12.7 mm	3 mm	45°	R>99.5%@1064nm	T>98%@808nm	>10 J/cm²	230 $	4 - 5 days
download PDF
i 042-6805HT	UV FS	ø 25.4 mm	6 mm	45°	R>99.5%@1064nm	T>98%@808nm	>10 J/cm²	285 $	4 - 5 days
download PDF
i 041-6200HT	UV FS	ø 12.7 mm	3 mm	0°	R>99.5%@1028-1080nm	T>98%@965-982nm	>10 J/cm²	266 $	4 - 5 days
download PDF
i 042-6200HT	UV FS	ø 25.4 mm	6 mm	0°	R>99.5%@1028-1080nm	T>98%@965-982nm	>10 J/cm²	315 $	4 - 5 days
download PDF
i 041-6202HT	UV FS	ø 12.7 mm	3 mm	22.5°	R>99.5%@1028-1080nm	T>98%@965-982nm	>3 J/cm²	266 $	4 - 5 days
download PDF
i 042-6202HT	UV FS	ø 25.4 mm	6 mm	22.5°	R>99.5%@1028-1080nm	T>98%@965-982nm	>3 J/cm²	315 $	4 - 5 days
download PDF
i 041-6205HT	UV FS	ø 12.7 mm	3 mm	45°	R>99.5%@1028-1080nm	T>98%@965-982nm	>3 J/cm²	303 $	4 - 5 days
download PDF
i 042-6205HT	UV FS	ø 25.4 mm	6 mm	45°	R>99.5%@1028-1080nm	T>98%@965-982nm	>3 J/cm²	351 $	4 - 5 days
download PDF

SUBSTRATE

Material	UV grade fused silica
Surface Flatness	λ/10 typical at 633 nm
Surface Quality	20-10 scratch & dig (MIL-PRF-13830B)
Diameter Tolerance	+0.00 mm -0.12 mm
Thickness Tolerance	±0.25 mm
Parallelism	30 arcsec
Chamfer	0.3 mm at 45° typical

COATING

Technology	Ion Beam Sputtering (IBS)
Clear Aperture	Exceeds central 85% of diameter
Coated Surface Flatness	λ/8 at 633 nm over 80% of diameter
Transmitted Wavefront Distortion (TWD)	λ/10 over clear aperture
Laser damage threshold	Measured for 10 ns pulse, 10 Hz, 1064 nm
Back side antireflection coated	R<0.1% at AOI=0° R<0.5% at AOI=45°

EKSMA Optics Dichroic Mirrors with High Transmission
71.83 kB

IBS coated for high power lasers
Laser damage threshold >10 J/cm², 8 nsec pulse, 1064 nm typical
Back side anti-reflection coated
Transmitted wavelength T>98%

Products

Information

Eksma Optics

Contacts

Address: Dvarcioniu st. 2B LT-10233 Vilnius, Lithuania
Phone: (+370) 5 272 99 00
Fax: (+370) 5 272 92 99
E-mail: [email protected]

© 2025 EKSMA Optics, UAB. All rights reserved.