Substrate
Material | UV grade fused silica |
S1 Surface flatness | λ/10 at 633 nm |
S1 Surface quality | 20-10 scratch&dig (MIL-PRF-13830B) |
S2 Surface quality | Commercial polish |
Diameter tolerance | +0.00 mm / -0.12 mm |
Thickness tolerance | ±0.25 mm |
Wedge | < 3 min |
Chamfer | 0.3 mm at 45° typical |
Coating
Technology | Ion Beam Sputtering (IBS) |
Adhesion and Durability | Per MIL-C-675A, Insoluble in lab solvents |
Clear apterture | Exceeds 85% of diameter |
Coated surface flatness | λ/8 at 633 nm over 80% of diameter |
Laser Induced Damage Threshold | Measured at design wavelength, 50 fs pulse, 100 Hz |
Group Delay Dispersion | |GDD| < 30 fs2 |
EKSMA Optics High Power IBS Coated Mirrors
126.56 kB |
New ultra high damage threshold laser mirrors are designed for applications with femtosecond lasers. These mirrors are produced using advanced IBS coating technology. Mirrors design wavelengths include 515 nm, 800 nm, 1030 nm and broadband 720-880 nm range with reflection values R>99.8%.
Laser induced damage threshold was measured at mirror design wavelength with 50 fs pulse, 100 Hz under ISO standard 21254-2 1000-on-1 conditions.