Lithium Iodate – LiIO3 Crystals

Applications

  • Harmonic generators
  • Thin LiIO3 for autocorrelation measurements

EKSMA OPTICS offers:

  • The mass production of LiIO3 crystals
  • Attractive discounts for OEM customers
  • Different shapes (slabs, cylinders, Brewster ends) are available
  • Standard open ring holders
  • Recoating and repolishing service
  • AR, BBAR and P - coatings subject to customer's choice
  • P-coatings optimised at pump wavelengths
  • BBAR coatings for wavelength tuned Ti:Sapphire and other lasers
Delivery

Estimated delivery time: from4 - 5 days

W, mm
L, mm
H, mm
θ
Coating
Code W, mm L, mm H, mm θ Coating Price Delivery Add to cart
LiIO3-1118-02 4 2 4 21 BBAR/BBAR@1064-1510 nm Request 4 - 5 days To cart
LiIO3-1118-03 4 3 4 21 BBAR/BBAR@1064-1510 nm Request 4 - 5 days To cart
LiIO3-1118-05 10 2 10 21.5 P/P@800-1300 nm Request 4 - 5 days To cart
LiIO3-0722-01H 6 6 0.3 23 BBAR/BBAR@700-1800 nm Request 4 - 5 days To cart
Delicious
Crystal structure hexagonal
Point group 6
Density, g/cm3 4.487
Mohs hardness 3.5–4.0
Transparency range, nm 280–4000
Absorption at 1064 nm, cm-1 < 0.05
Refractive indices at 1064 nm no = 1.8571, ne = 1.7165
                                 at 800 nm no = 1.8676, ne = 1.7245
                                 at 532 nm no = 1.8982, ne = 1.7480
Phase matching range for Type 1 SHG, nm 570–4000
Acceptances for Type 1 SHG at 1064 nm
                                  Angular, mrad×cm 0.77
                                  Spectral, cm-1×cm 12.74
Walk-off for Type 1 SHG at 1064 nm, mrad 74.30
Nonlinear optical coefficient d15, pm/V 2.2 (at 1064 nm)
Effective nonlinearity dooe = d15sinθ
Damage threshold, MW/cm2 > 100 for TEM00, 1064 nm, 10 ns, 10 Hz
Wavelength dispersion of refractive indices (λ – in μm)
no2 =2.083648+ (1.332068λ2/(λ2-0.035306))-0.008525λ2
 no2=1.673463+(1.245229λ2/(λ2-0.028224))-0.003641λ2

 